Thread-locking Adhesive

Anaerobic thread-locking adhesives can make thermosetting plastics with different strength after curing at room temperature, and the threaded fastener is resistant to impact, vibration, corrosion with no leakage and no rust. It can replace the mechanical locking devices such as spring pad and cotter pin.



Technical parameters for small thread-locking adhesives


Product code

Typical uses

Before curing

Chemical uses

Flashing point ℃

After curing

`

Color

Viscosity GB/T2794-1995mPa.s

Density GB/T13354-1992mPa.s

g/cm3

Destabilizing moment /1 day

Destabilizing moment /7 days

Size of product

Order code

GB/T18747.1-2002N.m

GB/T18747.1-2002N.m

N.m working temperature

N·m

2578

Small threads below M5, Frequent removal

Blue

350

0.88

Volatile curing

13

0.8

10.5

-40~80

1kg/barrel

257088

Note: The most prominent feature is that it does not affect the plastic and paint that it comes into contact. The marking of the locked thread is obvious.
         It can be removed with 10% to 20% dismantling moment; after removal, it can also be reused by sizing the adhesive. The cured adhesive has good ductility and vibration resistance.
         The adhesive can be first dipped onto the thread and then screwed together the thread, or it can penetrate inside by sizing it on the surrounding area of the screw. 




Technical parameters of thread locking anaerobic adhesives


Product code

Typical use

Maximum filling gap mm

Before curing

After curing

Curing speed

Product Size

Order code

Color

Viscosity

GB/T2794-1995mPa.s

Density

GB/T13354-1992mPa.s

g/cm3

Destabilizing moment

GB/T18747.1-2002N.m

Average removal moment GB/T18747.1-2002N.m

Working temperature

Curing time min

Full curing time

h

 

2228

M2-M8,Removable

0.13

Purple

1200 thixotropic

1.05

6

4

-50~150

10~20

24

50ml/bottle

222028

 

2428

M8-M16,Removable

0.13

Blue

1700 thixotropic

1.05

12

5

-50~150

10~20

24

50ml/

250ml/bottle

242028

242058

 

2438

M8-M20,

Oily surface

0.13

Blue

2250 thixotropic

1.05

20

7

-50~150

10~20

24

50ml/bottle

250ml/bottle

243028

243058

 

2628

M10-M26,Permanent locking

0.13

Red

1800 thixotropic

1.10

22

30

-50~150

10~20

24

50ml/bottle

250ml/bottle

262028

263058

 

2718

M16-M26,Permanent locking

0.13

Red

500

1.12

27

30

-50~150

10~20

24

50ml/bottle

250ml/bottle

271028

271058

 

2728

Below M32, high temperature resistance 230℃

0.25

Red

9500

1.12

22

24

-50~150

20~30

24

50ml/bottle

250ml/bottle

272028

272058

 

2778

M24-M36, Permanent locking

0.25

Red

7000

1.12

30

30

-50~150

20~30

24

50ml/bottle

250ml/bottle

277028

277058

 

2908

Below M12, permeability

0.10

Green

12

1.08

10

26

-50~150

5~15

24

50ml/bottle

250ml/bottle

290028

290058

 

2048

Pre-coating, equivalent to 2628.2718

0.25

Red

16000 thixotropic

1.05

18

30

-50~150

5~12

72

500g/set

202058

 




Technical parameters of pipe thread sealing anaerobic adhesives


Product code

Typical use

Maximum diameter of the thread

mm

Before curing

After curing

Solid content %

Product size

Order code

Color

Viscosity

GB/T2794-1995mPa.s

Density

GB/T13354

-1992mPa.sg/cm3

Maximum sealing pressure

MPa

Sealing working pressure time

Working temperature

5458

Sealing of hydraulic pneumatic pipe thread

M36awl/awl

Purple

14000thixotropic

1.05

69.5

Medium

-50~150

_

50ml/bottle

250ml/bottle

545028

545058

5548

Sealing of the pipe thread of refrigerating machine

M36awl/awl, straight

Red

2500

1.05

71.0

Medium

-50~150

_

250ml/bottle

554058

5678

General use, sealing of the pipe thread of stainless steel pipes

M36awl/awl

White

550000

1.15

71.0

Instant

-50~200

_

50ml/bottle

250ml/bottle

567028

567058

5698

Sealing of hydraulic pneumatic pipe thread

M36straight/straight

Brown

420

1.05

67.0

Medium

-50~150

_

50ml/bottle

569028

5778

Sealing of pipe thread with large clearance

M36awl/straight

Yellow

24000 thixotropic

1.10

65.0

Instant

-50~150

_

50ml/bottle

577028




Technical parameters of plane sealing anaerobic adhesives


Product code

Typical use

Maximum filling gap

mm

Before curing

After curing

Curing speed

Size

Order code

Color

Viscosity GB/T2794-1995mPa.s

Density

GB/T13354-1992mPa.sg/cm3

Adhesive state

Maximum sealing pressure

MPa

working temperature

Curing time

min

Full curing time

h

5108

Solvent resistance and high temperature resistance

0.25

Pink

100000 thixotropic

1.1

Rigid

32

-50~200

2~4

24

50ml/bottle

300ml/bottle

510028

510058

5158

General use

0.25

purplish red

180000 thixotropic

1.1

Soft

30

-50~150

1~2

24

50ml/bottle

300ml/bottle

515028

515058

5188

Aluminum parts

0.25

Red

800000

thixotropic

1.1

Soft

30

-50~150

3~4

24

50ml/bottle

300ml/bottle

518028

518058



Technical parameters of retaining anorexic adhesives


Product code

Typical use

Maximum filling gapmm

Before curing

After curing

Curing speed

Product size

Color

Viscosity GB/T2794-1995mPa.s

Density

GB/T13354-1992mPa.sg/cm3

Shear strength

GB/T18747.2-2002MPa

Working temperature

Curing time

min

Full cuing time

h

Order code

6038

Slightly oily surface

0.13

Green

200

1.10

>20

-50~150

5~10

24

50ml/bottle

250ml/bottle

603028

603058

6098

Transition, interference coordination

0.13

Green

175

1.10

>15

-50~150

10~20

24

50ml/bottle

250ml/bottle

609028

609058

6208

Resistance to high temperature 230℃

0.30

Green

7500 thixotropic

1.15

>17

-50~230

10~20

24

50ml/

250ml/bottle

620028

620058

6488

Continuous resistance to high temperature

175℃

0.15

Green

500

1.25

>18

-50~175

5~15

24

50ml/bottle

250ml/bottle

648028

648058

6808

Gap, transition coordination

0.25

Green

1250

1.12

>19

-50~150

10~15

24

50ml/bottle

250ml/bottle

680028

680058

6608

Large gap0.5mm)

0.50

Silver

1200000

thixotropic

1.12

>15

-50~150

10~15

24

50ml/bottle

660028

6628

The sealing of bowl - shaped plug, coating by equipment

0.13

Red

3000 thixotropic

1.08

>14

-50~150

5~15

24

1Kg/barrel

662028

6868

The sealing of bowl - shaped plug, manual coating

0.13

Red

32000

thixotropic

1.08

>14

-50~150

5~15

24

50ml/bottle

1Kg/barrel

686058

662088




3268 structural bonding anaerobic adhesive


* It is used for bonding rigid materials, especially suitable for bonding ferrite magnetic steel of small motors, and also for bonding metal and glass, with matching accelerator 7648.
* It is a kind of high strength multi-purpose adhesive, which can provide the strength of epoxy resin and the curing rate of instantaneous drying adhesive. It has good solubility and can be cured in a few minutes, which is suitable for rapid fixation.



Product code

Order code

Packaging specification

Typical use

Color

Maximum filling gap mm

Viscosity

mpa·s@20RPM

Shear strength

Mpa

Temperature range

Curing speed (initial / full)

Recommended primer

Density

3268

326028

326088

50ml/bottle

250ml/bottle

Rapid initial curing purpose

amber

0.5

1800

≥15.2

-54℃ to 120℃

1 minute/24hours

7648

1.10




7648 anaerobic adhesive primer


Pale green transparent liquid
Anaerobic adhesive primer for general uses
The drying time is 30 -70 seconds and the life on the part is 30 days.
Promote the large gap curing of anaerobic adhesive, improve the curing speed at low temperature, and promote the curing of lazy surface.
Packaging specification
128g/ aerosol tank     Order code 764058
1L/ tank                 Order code 764088